Mechanical properties of Gelatin –Hydroxyapatite composite for bone tissue engineering

Authors

  • MJ Hossan Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka-1000
  • MA Gafur PP and PDC, Bangladesh Council of Scientific and Industrial Research (BCSIR), Dhaka
  • MM Karim Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka-1000
  • AA Rana Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka-1000

DOI:

https://doi.org/10.3329/bjsir.v50i1.23805

Keywords:

Hydroxiapatite, Thermomechanical analysis, Tensile strength, Tensile elongation

Abstract

In this study, hydroxyapatite (HAp) and gelatin (GEL) scaffolds were prepared to mimic the mineral and organic component of natural bone. The raw material was first compounded and resulting composite were molded into the petridishes. Using Solvent casting process, it is possible to produce scaffolds with mechanical and structural properties close to natural trabecular bone.The mechanical properties of composites were investigated by Thermo-mechanical analyzer (TMA), Vickers microhardness tester, Universal testing machine. It was observed that the composite has maximum tensile strength of 37.13MPa ( oven drying) and % elongation of 7.68 (Oven drying) and 2.04 (Natural drying) at 15% of Hap respectively. These results demonstrate that the prepared composite scaffold is a potential candidate for bone tissue engineering.

Bangladesh J. Sci. Ind. Res. 50(1), 15-20, 2015

Downloads

Download data is not yet available.
Abstract
1568
PDF
1636

Author Biography

MJ Hossan, Department of Applied Chemistry and Chemical Engineering, University of Dhaka, Dhaka-1000



Downloads

Published

2015-06-22

How to Cite

Hossan, M., Gafur, M., Karim, M., & Rana, A. (2015). Mechanical properties of Gelatin –Hydroxyapatite composite for bone tissue engineering. Bangladesh Journal of Scientific and Industrial Research, 50(1), 15–20. https://doi.org/10.3329/bjsir.v50i1.23805

Issue

Vol. 50 No. 1 (2015)

Section

Articles

License

Bangladesh Council of Scientific and Industrial Research (BCSIR) holds the copyright to all contents published in Bangladesh Journal of Scientific and Industrial Research (BJSIR). A copyright transfer form should be signed by the author(s) and be returned to BJSIR.

The entire contents of the BJSIR are protected under Bangladesh Council of Scientific and Industrial Research (BCSIR) copyrights.

Creative Commons Licence
BJSIR is an open access journal, and articles are distributed under the terms of the Creative Commons Attribution-NonCommercial License (CC BY-NC) Creative Commons Attribution-NonCommercial 4.0 International License which allows others remix, tweak, and build upon the articles non-commercially, and although their new works must also acknowledge and be non-commercial, they don’t have to license their derivative works on the same terms.